Graphite pellets

ABSTRACT

Air or gas ground graphite is formed into pellets by mixing with finely divided alumina, forming into a paste and then granulating or extruding. The pellets so formed can be used as air or gas ground graphite but with the advantage that the pellets can be in the form of a fixed bed. A typical application is a polishing treatment for lubricating oils to remove aromatics, heterocyclics, sulphur compounds and coloured materials.

[ GRAPHITE PELLETS [75] Inventors: John Roland Cracknell, Esher;

Aleksander Jerzy Groszek, London, both of England [73] Assignee: The British Petroleum Company Limited, London, England [22] Filed: Dec. 14, 1970 [21] Appl. No.: 98,029

[30] Foreign Application Priority Data Dec. 19, 1969 Great Britain 61922/69 [52] US. Cl 252/447, 208/307, 208/310 [51] Int. Cl Cl0g 25/00 [58] Field of Search 208/307, 299, 310; 252/447 [56] References Cited UNITED STATES PATENTS 2,573,726 11/1951 Porter et al 252/447 X v[ June 25, 1974 Primary Examiner-Patrick P. Garvin Attorney, Agent, or Firm-Morgan, Finnegan, Durham & Pine [57] ABSTRACT Air or gas ground graphite is formed into pellets by mixing with finely divided alumina, forming into a paste and then granulating or extruding. The pellets so formed can be used as air or gas ground graphite but with the advantage that the pellets can be in the form of a fixed bed. A typical application is a polishing treatment for lubricating oils to remove aromatics, heterocyclics, sulphur compounds and coloured materials.

3 Claims, No Drawings GRAPHITE PELLETS other hydrocarbons by contacting the mixture with graphite having a surface area of at least 50m /gm, to absorb selectively the normal hydrocarbons.

However gas or vacuum ground graphites suffer from the disadvantage that finely ground graphite can only be used in the form of a slurry.

It has now been found that the graphite can be 1 formed into pellets by compounding with a binder. The

pellets can be used in the form of a fixed bed and have the further advantage in that a counter-current process can be used.

Thus according to the present invention there is provided a composition of matter comprising graphite in the form of pellets with a binder comprising finely divided alumina said graphite being a vacuum or gas ground graphite having a surface area of 50 to 2,000 m /gm (BET).

By the term finely-divided alumina we mean alumina having a surface area in the range 1 to 1,000 m /gm.

The term alumina is intended to embrace both hydrated alumina and anhydrous alumina.

Preferably the alumina has a surface area in the range 100 to 600 m /gm.

The finely divided alumina'is preferably (i) a colloidal alumina manufactured by Du Font and sold under the name Baymal" and having a surface area of 350 m /gm, this material is a micro-crystalline fibrous boehmite and is a-alumina monohydrate or (ii) a colloidal alumina manufactured by Laporte and described as Dispersible alumina" and designated RD 12026. The preparation of the Baymal alumina is described in US. Pat. No. 2,915,475.

The US. Pat. No. 2,915,475 discloses the preparation of fibrous Boehmite (oz-alumina monohydrate) and describes the alumina as being in the form of small fibrils (the word fibril" meaning an individual crystalline particle) in the shape of laths, at least two of the dimensions of which are in the colloidal range. The laths have their two smaller dimensions in the range 3 to 15 nanometers whilst their axial ratio, their ratio between their length and smaller dimensions, falls in the range 50:1 to 150:1. Baymal which has a surface area of about 350 m /gm would have fibrils having their small dimensions at about 4 nanometers and lengths of between 200 and 600 nanometers. Depending on the conditions of manufacture the fibrils may agglomerate to give thread like aggregates called fibres which may show only partial colloidal properties.

The pellets may contain from 5 to 50 percent by weight of alumina binder preferably to 40 percent wt., and from 95 to 50 percent by weight of graphite, preferably 85 to 60 percent wt.

According to another aspect of the present invention there is provided a process for the preparation 'of graphite-containing pellets which process comprises intimately mixing a vacuum or gas-ground graphite powder having a surface are of 50 to 2,000 m lgm with a finely divided aluminabinder, working the mixture into a paste with a suitable liquid and granulating or extruding through a die.

The graphite and the alumina can be mixed either wet or dry. In dry mixing satisfactory results have been obtained byball milling but high speed mixing in, e.g., a Universal High Speed mixer Type TLEHK 8 made by Gunter Papenmeier AG. is preferred. In wet mixing it is preferred to mix using a High Speed Mixer or a colloid mill e.g. a colloid mill made by Premier Colloid Mills Ltd. using a gap of 1.016 X 10" m between the stones. The granulation can be effected by spreading the paste out on a tray, allowing to dry and breaking up the cake so formed.

After extrusion or granulation the extrudate or granules are preferably dried, broken up and sintered in nitrogen for 24 hours at 400C.

The extruded pellets thus prepared are mechanically strong and stable in hydrocarbon solvents such as toluene, n-heptane and iso-octane.

The graphite used to prepare the pellets is preferably ground graphite prepared by ball milling graphite in vacuum or a gas, e.g., air.

The grinding of the graphite gives small particles with a plate like graphite structure. Most of the surface area is contributed by the basal planes of the plates, but there is also a significant contribution made by the edges. For air ground graphite the ratio of basal plane surface area to edge surface area in a typical instance is about 4.5:].

As previously described the graphites thus produced have the capability of absorbing normal hydrocarbons on the basal plane surface area and polar compounds, e.g., aromatics, sulphur and nitrogen compounds on the edge surface area. By adjustment of the feedstock and process conditions as described hereunder, the selectivity for either type of compound can be varied.

Thus according to another aspect of the present invention a process for the separation of normal hydrocarbons and/or polar compounds from their mixtures with other hydrocarbons comprises contacting the mixture with graphite pellets as hereinbefore defined to selectively adsorb said normal hydrocarbons and/or polar compounds.

The graphites before compounding with the binder preferably have a surface area of at least 50 square metres per gram and more preferably have a surface area of at least 300 square metres per gram.

The feed mixture for the process may be a petroleum distillate or residue boiling above 30C, particularly a fraction in the waxy distillate boiling range i.e. 300 to 700C or a waxy raffinate or a dewaxed raffinate. The feed may be a straight run fraction or a waxy raffmate obtained after a selective solvent treatment with, e. g., furfural to remove aromatics. The feed may also be a solvent treated dewaxed lubricating oil fraction or bydrocracked gas oil the treatment in this case being a finishing treatment to improve colour and oxidation stability.

The process can also be used for removing polynuclear aromatic compounds, e.g., 3,4, benzo pyrene from lubricating oils and waxy distillates.

The absorption and desorption stages of the process of the invention are preferably carried out in the presence of liquids in which the adsorbed and subsequently desorbed components are soluble. These liquids may be the same or different. Thus, the liquid may comprise a single paraffin hydrocarbon, such as n-heptane or isooctane, or it may comprise a mixture of hydrocarbons including refinery streams such as Primary Flash Distillate or an aromatic or alcoholic solvent may be used. The solvent used for dewaxing is preferably a polar solvent since such solvent promotes the absorption of non-polar compounds, such, as waxes, including long chain n-paraffins. For the removal of polar compounds, the preferred solvent is a n-paraffin.

The adsorption stage of the process of the invention may be performed at a temperature of from -50C to 200C. If a mixture of paraffins, aromatics or alcohols is used its boiling range should be within this range. Hydrocarbons whose atmospheric boiling point is outside this range may be used at sufficient pressure to achieve a boiling point within the range quoted, provided that the description temperature is not above the critical temperature. Thus, for example, liquified propane and butane (L.P.G.) may be used under certain conditions.

For processing waxy raffinates and distillates a solvent is preferred. For a mobile liquid feedstock such as gas oil or kerosene no solvent is required.

The loading of the graphite with the absorbedcomponents will depend on the nature of the feed, but should desirably be as low as possible. The loading expressed as graphitezfeed ratio by wt is preferably less than 1:2, and more preferably less than 1:1 wt. The ratio of absorbed components to graphite may, however, be as low as 1:100. When refining waxy raffinates or distillates with dewaxing as the prime objective the overall graphite:feed ratios will usually be in the range 1:1 to 10:1. If a multistage batch treatment is being used the individual stage graphite:feed ratios may be in the range 0.5:! to 4:1.

When applying a polishing treatment to a dewaxed raffmate with the object of removing aromatics, heterocyclics, sulphur compounds and coloured materials, the overall graphitezfeed ratios may be in the range 0.5:1 to 4:1.

The feed solvent/feed ratios can vary from :1 and 50:1 by wt. Suitable contact times between the graphite and the feed may be from 1 minute to 24 hours. The adsorption of n-paraffins is promoted by low temperatures within the stated range, and the preferential adsorption of aromatics by higher temperatures. Thus, the temperature should not be above 100C and preferably from 0 to 50C if it is desired to adsorb paraffms. The temperature may be above 30C, and preferably from 50 to 200C where aromatics are to be adsorbed.

- range of 100 to 400C.

Alternatively, certain feedstocks can be treated over the graphite alumina adsorbent in the gas phase.

The pressure at which desorption is carried out should be such as to maintain the eluting material in the liquid state and will accordingly be within the range 10 to 3,000 psig. It will of course be determined by the vapour pressure of the eluting material at the desorption temperature. The contact time will be within the range 1 to 120 minutes. The solvent desorbate ratio is preferably from 11:] to 100:1.

The method is desirably carried out in a cyclic type of operation, for example, by percolating the feed mixture together with liquid through a bed of graphite pellets, removing non-adsorbed feed material and liquid from the bed stripping the liquid from the nonadsorbed feed material, desorbing the adsorbed material from the graphite with the liquid, removing the desorbed material and liquid from the bed, stripping liquid from the desorbed material, and re-contacting the graphite with the feed mixture. In such a fixed bed type of operation reaction conditions, in particular liquid flow rate, should be chosen so that the pressure drop across the bed is not excessive.

1n the case of preparation of lubricating oil basestocks, the feedstock may be treated by any number of adsorption/desorption cycles to give a desired pourpoint and viscosity index. The pour point of the treated material will decrease as the extent of removal of adsorbed materials increases, but the yield will also decrease. Waxy raffinate fractions treated by the process of the invention have in general higher viscosity indexes, lower cloud and pour points and lower sulphur contents than fractions obtained by conventionally treating similar feedstocks. They also have better response to oxidation inhibitors. In addition to the oil products obtained, the absorbed and subsequently desorbed material, i.e., normal paraffins and/or aromatics may be of use, particularlyif it is waxy paraffinic or aromatic hydrocarbon material.

The invention is illustrated by the following examples.

EXAMPLE 1 A Kuwait waxy distillate having a pour point of 38C viscosity at 38C 220 centistokes viscosity index 67 60C 64.34 do. sulphur 3.18% wt 77C 31.57 do. 99C 15.09 do.

was mixed with the pelletted graphite and iso-octane under the following conditions:

Loading by wt 5:1 (pellets:distillate) Solvent iso-octane at 20 ml per g feedstock Temperature ambient Contact time 24 hr.

The graphite pellets were prepared by mixing gms of graphite obtained from Solid Lubricants Limited prepared by grinding in air in a cascade ball mill to a surface area of 375m /gm (B.E.T.) with 25 gms ofBaymal alumina and then milling the dry solids for 10 minutes. The mixture was then worked into a thick paste by adding water and extruded through a 3.175 X 10 M die. The extrudate was dried in air, broken up into pel- 6 lets of size one-eighth inch diameter and sintered in ni- Table l trogen for 24 hours at 400C to yield pellets itsize oneeighth inch diameter. The treated distillate (obtained in Micm SUI hur T t I A o a 55 percent wt yield) was separated from the pellets by Fraction Yield Pour ASTM Cori tent Nitrogen filtration and removal of solvent and had the following 5 g g g Colour Wt pp CA properties:

Viscosity at 38C 164.52 c St (220) 2 52-06 64334) 1 405.6 5 05 0.67 9 2.6 99 C 115-091 2 1029.0 1.0 0.97 31 3.5 W "4" (67) 3 1016.5 10 1.5 1.03 66 3.4 Pour po1nt(m1cro) +4C (+38C) 1O 4 979.4 [04 85 38 5 1014.0 1.5 1.03 100 4.2 6 624.0 1.5 1.04 105 3.8 Figures in brackets refer to the original d1st1llate. 7 [27m 21) 1.04 l m 3'6 8 944.0 1.06 110 3.7 EXAMPLE 2 9 1343.0 2.0 1.06 115 3.6

. 2. 3. A finished Kuwait/1 meg lubricating 011 having a vrs- 5 Feed 10 5 I O6 6 cosity of l 10 contistokes at 100F and a viscosity index of 95 determmed m accordance ASTM D 7 After passing the oil, the column was washed with isowas Percolated through a bed of 14400 5 graphlt e octane at 250C and 274 g of waxes and aromatics realumma Crushed exlrudate under the followmg condl' covered. After the desorption the feedstock was percotlons: 20 lated again and 2 fractions collected comprising a total Solvent iso-octane at 3 ml per g feedstock f 1 855 g as Shown i T bl 2 Temperature ambient Space velocity 0.365 vol/vol/hour contact time 2.74 hours wtof. adsorbent g length 45 cms. I 7 able 2 g The graphite alumina adsorbent was prepared by 25 mixing 3 parts by weight of graphite obtained from Second Run Solid Lubricants Limited and prepared by grinding in I O m air in a cascade ball mill to a surface area of 375 m /gm Fraction Cumulative Graphite ASTM s '72 N ppm CA (BET) with 1 part of Baymal alumina and then ball Colour milling the dry solids for 10 minutes. The mixture was 1 545 06H 10 24 then worked into a thick paste and extruded through a 2 1855 1.9;. 66 3.175 X 10' M die. The extrudate was dried in air, sintered in nitrogen at 400C for 24 h and crushed and sieved to yield 14-100 mesh BSS adsorbent. EXAMPLE 3 The treated oil was collected in 9 fractions havin the h T bl l g EXTRACTION OF POLYNUCLEAR COMPOUNDS pmpemes S a e BY GRAPHITE/ALUMINA The results show that treatment with the graphite pellets improves the colour stability of the lubricating oil The pellets were prepared exactly as in Example 2 and removes aromatics, sulphur and nitrogen combut alumina manufactured by Laporte havingasurface pounds. 40 area of 2m /gm was used in place of Baymal Alumina. Overall Yield of unadsorbed oil 97 percent The pellets were the same size as in Example 2 viz Overall graphitezfeed oil ratio 0.082l:1 4-100 mesh B.S.S.

Oil Total UV Absorbance 3,4-Benzopyrene 280-400 mu Ug/kg X (a) A middle East waxy 32.0 750 distillate. The procedure of Example 2 was re peated but, 5 parts by weight of oil treated with 1 part of graphite/ alumina at C withsolvent 9.1 30 (b) Feed oil 9.4 150 As in (a) above, 5 parts of oil treated with 1 part of graph ite/alumina at 50C without solvent 6.2 20 As above, 1:] treatment with graphite/ alumina at 20C in isooctane 0.6 10 (c) SAE 10 lubricating oil prepared by hydrogeneration of a Kuwait vacuum distillate 2.7 100 As in (a) and (b) above 5 parts of oil treated with 1 part of graphite lalumina at 50C no solvent 0.] 10

X determined by liquid chromatography and UV spectroscopy. determined by FDA 121.25119tc)v The oil used in Example 3 (a) has the following inspection data:

Kinematic viscosity at ll-' 20.5 centistokcs l40F 9.6 do. 2HlF 3.86 do.

Specific Gravity 60/60 0.90l

The oil used in Example 3 (b) gave the following Vacuum Engler distillation data.

Initial listing point 343 109i distilled 383 50% distilled 414 907: distilled 450 Final listing point 472 Kinematic viscosity at 100F 20.5 centistokes l40F 9.6 centistokes 2l0F 3.86 centistokes Specific Gravity 60/60 0.8805.

EXAMPLE 4 TABLE I Graphite/Alumina GB 300 6 885 mesh BET Surface Area, m /g 3S5 Bulk Density Maximum 0.61 0.52

gms/cc gms/cc Separation of a Waxy Raffinate having a viscosity of 1 1O centistokes at 100F and a viscosity index of 95 determined in accordance with ASTM'D 2270 over a column'of Graphite alumina absorbent. A column 89 cen- GRAPHITE TREATMENT OF A HYDROCRACKED 25 timetres long and 5.7 centimetres square cross section GAS OlL The pellets were prepared exactly as described in Example 3 and the hydrocracked gas oil, boiling range 225C to 370C, was percolated through graphite/alumina pellets without solvent at room temperature, the products being Collected at oil to graphite ratios of 20:1 and :1.

The percolated oils have been found to be much lighter in colour and had a significantly greater stability to light and heat compared with the feedstock as shown in the table below.

Percolated Oils was filled with 300 grams of 6-25 BSS mesh crushed graphite/alumina extrudate.

A solution of 5 6.25 grams of the waxy Raffmate of Kuwait origin in 500 milli-liters of isooctane was pumped through the column at a flow rate of 200 mls per hour and a residence time time of 2 hours. The removal of fractions of the unadsorbed oil was effected by pumping isooctane through the Column. Equal volumes of solution issuing from the Column gave the following yields and pour points when the oil was isolated. The temperature of the elution was 22C.

Test Feedstock Oil to Oil to Graphite Ratio Graphite Ratio Colour, ASTM 3.5 0.5 0.5 Exposure to sunlight, light brown no deposit, no deposit, l day on window sill deposit oil clear oil clear *DEF 2060 test, Method l6 (heating at 2lOF for 16 hours) v Total sediment, mg/lOOm 0.23 O.l 0.06

' Ministry of Defence test.

These results showthat polishing of gas oils by per- TABLE ll colation through graphite/alumina absorbents in- V H A v I creases substantially the" StabllltlCS tOllght and heat. Absorbent Graphite 7517 pechiney G 300 alumina 25% 6-25 855 mesh.

. weight 300 gms I EXAMPLE 5 Eluent isooctane Flow rate 200 mls/hr PREPARATION OF GRAPHITE/ALUMINA gff ngqlTlme i n glolum n 2 hours arge l Uwfllt aXy ABSORBENT Raft-mie- .2.V .2. ......-2- HA t Y Charge weight 56.25 grams The graphite, grams, was mixed in a dry state with a Pom! of i 25 grams of the alumina, which has a dispersible type 33533? 0 ee GB 300 obtained from Pechiney St Gobain. 65 Eluted y jw e The graphite had a surface area of 380 m /gm and the gtf 'gg f Perm" s alumina 300 111 m. Fraction 2 Weight percent 23.5

TABLE Il-Continued We claim:

Pour Point F s l. A composition of matter in the form of pellets con- U sisting essentially of 95 to 50 percent wt. of a vacuum Fraction 4 Weight percent 5 or gas ground graphite having a surface area of 50 to Pour point 2 Fraction 5 Weight percent 53 2000 m gm l BET) and as a binder, 5 to 50 percent wt. Pour 5 5 of a finely divided alumina. Fraction 6 weight percent 3.9 v Pour point 50 2. A composition as cla med in claim 1 where n the g n g Pervcm 2 alumina has a surface area of 100 to 600 m /gm.

OUl' POll'l v i Fragtion eluted with hot 1O 3. A composition as claimed in claim 1 wherein the Ethylene Dichloride 150 c wt% 14.6 pellets have a particle size in the range 4 to 200 mesh Pour point "F 100 BSS 

2. A composition as claimed in claim 1 wherein the alumina has a surface area of 100 to 600 m2/gm.
 3. A composition as claimed in claim 1 wherein the pellets have a particle size in the range 4 to 200 mesh BSS. 